G42

G42

Bonding paste smooth without fibres


Adhesive bonding paste viracolor made from unsaturated polyester resins and mineral fibres.
Used in the composite sector for samm angles and chines smoothing, gluing of inserts and core materials.

SUPPORTS

Recommended: Gelcoat, polyester and vinylester fibreglass, wood, various types of foam.

GENERAL INSTRUCTIONS FOR USE

Apply on well sanded and cleaned surfaces;
Make sure the substrate is free of dust, fibres, dirt and surface condensation.
Carefully mix the bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required.
The recommended temperature range is between 16 and 28°C. The product contains viracolor.
It must be applied manually with a spatula after careful mixing the hardener or by machine.
For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums, the use of a pressing plate extruder-mixer guarantees the best mixing efficiency.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


Mould - Lamination
Lamination - Assembling

See other Bonding Pastes



G32

G32

Bonding paste smooth with fibres


Adhesive bonding paste viracolor made from unsaturated polyester resins, reinforced with mineral fibres.
Used in the composite sector for its excellent adhesion in bonding laminates and inserts of various types.
The reinforcing fibers give this product high mechanical resistance, making it suitable for bonding floors and cielings, filling of the strips and gluing inserts.

SUPPORTS

Recommended: polyester and vinylester fibreglass, wood, various types of foam.

GENERAL INSTRUCTIONS FOR USE

Apply on well sanded and cleaned surfaces;
Make sure the substrate is free of dust, fibres, dirt and surface condensation.
Carefully mix the bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required.
The recommended temperature range is between 16 and 28°C. The product contains viracolor.
It must be applied manually with a spatula after careful mixing the hardener or by machine.
For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums, the use of a pressing plate extruder-mixer guarantees the best mixing efficiency.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


Mould - Lamination
Lamination - Assembling

See other Bonding Pastes



B15F

B15F

Bonding paste flex with fibres


Adhesive bonding paste with high elasticity based on unsaturated polyester resins and reinforced with fibres.
Used in the composite sector for its excellent adhesion for the bonding of laminates and inserts of various types.

SUPPORTS

Fiberglass polyester and vinylester, wood, various types of foam.

GENERAL INSTRUCTIONS FOR USE

Apply on well sanded and cleaned surfaces;
Make sure the substrate is free of dust, fibres, dirt and surface condensation.
Carefully mix the mastic with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required.
The recommended temperature range is between 16 and 28°C.
It must be applied manually with a spatula after careful mixing the hardener or by machine.
For quantities over 5 kg, mixing with a stirrer is recommended, while for 200 l drums, the use of a pressing plate extruder/mixer guarantees the best mixing efficiency.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time.


Packaging

Type of use


Mould - Lamination
Lamination - Assembling

See other Bonding Pastes



BV10S

BV10S

Light vinylester bonding paste slow


BV10 series bonders are certified by RINA (Type Approval DIP146622CS)

Adhesive bonding paste based on unsaturated vinylester resins, microspheres and light reinforcing fillers, characterized by a specific formulation for long gel time, high mechanical properties and low shrinkage.
Specifically formulated for the use of large vacuum bags and for bonding sheets and inserts in Balsa, PVC, PET, PIR and polyurethane foam, is easily spatulable and deaerable without dripping from vertical surfaces. Under pressure or vacuum it flows easily, saturating every crack and cavity of the foam thus ensuring high mechanical, thermal and chemical properties to the sandwich laminate. The low specific weight of its formulation is combined with limited shrinkage during hardening and excellent adhesion performance even on high density foams.

SUPPORTS

Properly prepared and cleaned polyester and vinylester fiberglass laminates.

GENERAL INSTRUCTIONS FOR USE

Product particularly suitable for applications in the summer months. Can be applied directly on freshly laminated surfaces free of dust, fibers, dirt and condensation. Completely hardened surfaces must instead be sanded and cleaned thoroughly. Check the suitability for use on surfaces obtained from paraffin resins. Mix the product directly in its packaging and mix it with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required (See page 8 of “Core Adhesives for Foams guidelines”). The recommended temperature range is between 18 and 28°C. The product contains viracolor in order to verify the homogeneous dispersion of the peroxide. It can be applied manually with a spatula, for quantities over 5 kg, mixing with a whisk is recommended, while for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency. The product has also been formulated to be sprayable, where the large surfaces of components or the rapid cycles of mass production require it. For further details and recommended application procedures, refer directly to the “Core Adhesives for Foams guidelines”, available at the INTEC Technical Assistance Center. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time.


Packaging

Type of use


MOULD-LAMINATION
LAMINATION-ASSEMBLING

See other Bonding pastes for core materials



BV10R

BV10R

Light vinylester bonding paste rapid


BV10 series bonders are certified by RINA (Type Approval DIP146622CS)

Adhesive bonding paste based on unsaturated vinylester resins, microspheres and light reinforcing fillers, characterized by high mechanical and thermal properties, and low shrinkage. Specifically formulated for the use of large vacuum bags and for bonding sheets and inserts in Balsa, PVC, PET, PIR and polyurethane foam, is easily spatulable and deaerable without dripping from vertical surfaces. Under pressure or vacuum it flows easily, saturating every crack and cavity of the foam thus ensuring high mechanical, thermal and chemical properties to the sandwich laminate. The low specific weight of its formulation is combined with limited shrinkage during hardening and excellent adhesion performance even on high density foams.

SUPPORTS

Properly prepared and cleaned polyester and vinylester fiberglass laminates.

GENERAL INSTRUCTIONS FOR USE

Product particularly suitable for applications in the winter months. Can be applied directly on freshly laminated surfaces free of dust, fibers, dirt and condensation. Completely hardened surfaces must instead be sanded and cleaned thoroughly. Mix the product directly in its packaging and mix it with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required (See page 8 of “Core Adhesives for Foams guidelines”). The recommended temperature range is between 14 and 18°C. The product contains viracolor in order to verify the homogeneous dispersion of the peroxide. It can be applied manually with a spatula, for quantities over 5 kg, mixing with a whisk is recommended, while for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency. The product has also been formulated to be sprayable, where the large surfaces of components or the rapid cycles of mass production require it. For further details and recommended application procedures, refer directly to the “Core Adhesives for Foams guidelines”, available at the INTEC Technical Assistance Center. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time.


Packaging

Type of use


MOULD-LAMINATION
LAMINATION-ASSEMBLING

See other Bonding pastes for core materials



BV10

BV10

Vinylester bonder light


BV10 series bonders are certified by RINA (Type Approval DIP146622CS)

Lightweight adhesive bonding paste based on unsaturated vinylester resins, microspheres and light reinforcing fillers, characterized by high mechanical and thermal properties, and low shrinkage. Specifically formulated for bonding sheets and inserts in Balsa, PVC, PET, PIR and polyurethane foam, is easy to apply, spread with spatula, easily deaerate and stick to the surface without dripping from vertical surfaces. Under pressure or vacuum it flows easily, saturating every crack and cavity of the foam thus ensuring high mechanical, thermal and chemical properties to the sandwich laminate. The low specific weight of its formulation is combined with limited shrinkage during hardening and excellent adhesion performance even on high density foams.

SUPPORTS

Properly prepared and cleaned polyester and vinylester fiberglass laminates.

GENERAL INSTRUCTIONS FOR USE

Can be applied directly on freshly laminated surfaces free of dust, fibers, dirt and condensation. Completely hardened surfaces must instead be sanded and cleaned thoroughly. The suitability for use on surfaces obtained from paraffin resins must be checked. Mix the product directly in its packaging and mix it with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required. The recommended temperature range is between 14 and 28°C. The product contains viracolor in order to verify the homogeneous dispersion of the peroxide. It can be applied manually with a spatula, for quantities over 5 kg, mixing with a whisk is recommended, while for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency.
The product has also been formulated to be sprayable, where the large surfaces of components or the rapid cycles of mass production require it. For further details and recommended application procedures, refer directly to the “Core Adhesives for Foams guidelines”, available at INTEC Technical Assistance Center.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time


Packaging

Type of use


MOULD-LAMINATION
LAMINATION-ASSEMBLING

See other Bonding pastes for core materials



B10R

B10R

Light polyester bonding paste


Lightweight adhesive bonding paste based on unsaturated polyester resins, microspheres and light reinforcing fibers, characterized by a rapid gel time.
Specifically formulated for the composite sector for bonding core materials and inserts in Balsa, PVC, PET, PIR and polyurethane foam. It is easy to apply, spread with spatula, easily deaerate and stick to the surface thanks to the excellent tixotropy. Under pressure or vacuum it flows easily saturating every crack and cavity of the foam thus ensuring high mechanical, thermal and chemical properties to the sandwich laminate. The low specific weight of its formulation is combined with limited shrinkage during hardening and excellent adhesion performance even on high density foams.

SUPPORTS

Recommended: properly prepared and cleaned polyester and vinylester fiberglass laminates.

GENERAL INSTRUCTIONS FOR USE

The product can be applied directly to freshly laminated surfaces free of dust, fibers, dirt and condensation. Completely hardened surfaces must instead be sanded and cleaned thoroughly. The suitability for use on surfaces obtained from paraffin resins must be checked. Mix the product directly in its package with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required. The recommended temperature range is between 16 and 28°C. The product contains viracolor in order to verify the homogeneous dispersion of the peroxide. It can be applied manually with a spatula or by machine For quantities over 5 kg, mixing with a whisk is recommended. The product has also been formulated to be sprayable, where the large surfaces of components or the rapid cycles of mass production require it. For further details and recommended application procedures, refer directly to the “Core Adhesives for Foams guidelines”, available at INTEC’s Technical Assistance Center.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time.


Packaging

Type of use


MOULD-LAMINATION
LAMINATION-ASSEMBLING

See other Bonding pastes for core materials



B10

B10

Light polyester bondig paste


Lightweight adhesive bonding paste based on unsaturated polyester resins, microspheres and light reinforcing fillers.
Specifically formulated for the composite sector for bonding core materials and inserts in Balsa, PVC, PET, PIR and polyurethane foam. It is easy to apply, spread with spatula, easily deaerate and stick to the surface thanks to the excellent tixotropy. Under pressure or vacuum it flows easily saturating every crack and cavity of the foam thus ensuring high mechanical, thermal and chemical properties to the sandwich laminate. The low specific weight of its formulation is combined with limited shrinkage during hardening and excellent adhesion performance even on high density foams.

SUPPORTS

Recommended: properly prepared and cleaned polyester and vinylester fiberglass laminates.

GENERAL INSTRUCTIONS FOR USE

The product can be applied directly to freshly laminated surfaces free of dust, fibers, dirt and condensation. Completely hardened surfaces must instead be sanded and cleaned thoroughly. The suitability for use on surfaces obtained from paraffin resins must be checked. Mix the product directly in its package with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required. The recommended temperature range is between 16 and 28°C. The product contains viracolor in order to verify the homogeneous dispersion of the peroxide. It can be applied manually with a spatula or by machine. For quantities over 5 kg, mixing with a stirrer is recommended,
while for 200 l drums, the use of a pressing plate extruder/mixer
guarantees the best mixing efficiency. The product has also been formulated to be sprayable, where the large surfaces of components or the rapid cycles of mass production require it. For further details and recommended application procedures, refer directly to the “Core Adhesives for Foams guidelines”, available at INTEC’s Technical Assistance Center. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time.


Packaging

Type of use


MOULD-LAMINATION
LAMINATION-ASSEMBLING

See other Bonding pastes for core materials



B07

B07

Extra light polyester bonding paste


Extra light adhesive bonding paste based on unsaturated polyester resins, microspheres and ultralight reinforcing fillers.
Specifically formulated for the composite sector for bonding core materials and inserts in Balsa, PVC, PET, PIR and polyurethane foam, in constructions that require maximum reduction of weights. It is easy to apply, spread with spatula, easily deaerate and stick to the surface thanks to the excellent tixotropy. Under pressure or vacuum, it flows easily, saturating every crack and cavity of the foam thus ensuring high mechanical, thermal and chemical properties to the sandwich laminate. Characterized by an extra lightweight, it also adds: low shrinkage during hardening and excellent adhesion performance even on high density foams.

SUPPORTS

Recommended: properly prepared and cleaned polyester and vinylester fiberglass laminates.

GENERAL INSTRUCTIONS FOR USE

The product can be applied directly to freshly laminated surfaces free of dust, fibers, dirt and condensation. Completely hardened surfaces must instead be sanded and cleaned thoroughly. The suitability for use on surfaces obtained from paraffin resins must be checked. Mix the product directly in its package with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required. The recommended temperature range is between 16 and 28°C. The product contains viracolor in order to verify the homogeneous dispersion of the peroxide. It can be applied manually with a spatula or by machine. For quantities over 5 kg, mixing with a stirrer is recommended, while for 200 l drums, the use of a pressing plate extruder/mixer guarantees the best mixing efficiency. The product has also been formulated to be sprayable, where the large surfaces of components or the rapid cycles of mass production require it. For further details and recommended application procedures, refer directly to the “Core Adhesives for Foams guidelines”, available at INTEC’s Technical Assistance Center. In its original packaging, the product can be used for 8 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time.


Packaging

Type of use


MOULD-LAMINATION
LAMINATION-ASSEMBLING

See other Bonding pastes for core materials



GV23

GV23

Vinylester bonding paste for lamination - rapid


Vinylester bonding paste reinforced with highly reactive glass microfibres with a fast gel time, characterized by remarkable thermal and mechanical properties other than excellent adhesion and flexibility Specifically formulated to assemble and repair moldings and fiberglass laminates, during the lamination phases for filling strips and joints thanks to its excellent adhesion to the substrate and its high mechanical and anti-osmosis properties. Contains viracolor.

SUPPORTS

Recommended: Fiberglass polyester and vinylester laminates.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure that the substrate is free of dust, fibers, dirt and surface condensation. Carefully mix the vinylester bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount required depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C. It must be applied manually with a spatula. For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


LAMINATION-ASSEMBLING
MOULD-LAMINATION
BODY-FINISHING

See other Bonding Pastes