G42

G42

Bonding paste smooth without fibres


Adhesive bonding paste viracolor made from unsaturated polyester resins and mineral fibres.
Used in the composite sector for samm angles and chines smoothing, gluing of inserts and core materials.

SUPPORTS

Recommended: Gelcoat, polyester and vinylester fibreglass, wood, various types of foam.

GENERAL INSTRUCTIONS FOR USE

Apply on well sanded and cleaned surfaces;
Make sure the substrate is free of dust, fibres, dirt and surface condensation.
Carefully mix the bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required.
The recommended temperature range is between 16 and 28°C. The product contains viracolor.
It must be applied manually with a spatula after careful mixing the hardener or by machine.
For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums, the use of a pressing plate extruder-mixer guarantees the best mixing efficiency.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


Mould - Lamination
Lamination - Assembling

See other Bonding Pastes



G32

G32

Bonding paste smooth with fibres


Adhesive bonding paste viracolor made from unsaturated polyester resins, reinforced with mineral fibres.
Used in the composite sector for its excellent adhesion in bonding laminates and inserts of various types.
The reinforcing fibers give this product high mechanical resistance, making it suitable for bonding floors and cielings, filling of the strips and gluing inserts.

SUPPORTS

Recommended: polyester and vinylester fibreglass, wood, various types of foam.

GENERAL INSTRUCTIONS FOR USE

Apply on well sanded and cleaned surfaces;
Make sure the substrate is free of dust, fibres, dirt and surface condensation.
Carefully mix the bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required.
The recommended temperature range is between 16 and 28°C. The product contains viracolor.
It must be applied manually with a spatula after careful mixing the hardener or by machine.
For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums, the use of a pressing plate extruder-mixer guarantees the best mixing efficiency.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


Mould - Lamination
Lamination - Assembling

See other Bonding Pastes



B15F

B15F

Bonding paste flex with fibres


Adhesive bonding paste with high elasticity based on unsaturated polyester resins and reinforced with fibres.
Used in the composite sector for its excellent adhesion for the bonding of laminates and inserts of various types.

SUPPORTS

Fiberglass polyester and vinylester, wood, various types of foam.

GENERAL INSTRUCTIONS FOR USE

Apply on well sanded and cleaned surfaces;
Make sure the substrate is free of dust, fibres, dirt and surface condensation.
Carefully mix the mastic with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required.
The recommended temperature range is between 16 and 28°C.
It must be applied manually with a spatula after careful mixing the hardener or by machine.
For quantities over 5 kg, mixing with a stirrer is recommended, while for 200 l drums, the use of a pressing plate extruder/mixer guarantees the best mixing efficiency.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C. Some drift may occur in gel time.


Packaging

Type of use


Mould - Lamination
Lamination - Assembling

See other Bonding Pastes



GV23

GV23

Vinylester bonding paste for lamination - rapid


Vinylester bonding paste reinforced with highly reactive glass microfibres with a fast gel time, characterized by remarkable thermal and mechanical properties other than excellent adhesion and flexibility Specifically formulated to assemble and repair moldings and fiberglass laminates, during the lamination phases for filling strips and joints thanks to its excellent adhesion to the substrate and its high mechanical and anti-osmosis properties. Contains viracolor.

SUPPORTS

Recommended: Fiberglass polyester and vinylester laminates.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure that the substrate is free of dust, fibers, dirt and surface condensation. Carefully mix the vinylester bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount required depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C. It must be applied manually with a spatula. For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


LAMINATION-ASSEMBLING
MOULD-LAMINATION
BODY-FINISHING

See other Bonding Pastes



GV22

GV22

Vinylester bonding paste for lamination


Vinylester bonding paste reinforced with glass microfibers, characterized by remarkable thermal and mechanical properties other than excellent adhesion and flexibility. Specifically formulated to assemble and repair fiberglass laminates, during the lamination phases for filling strips and joints thanks to its excellent adhesion to the substrate and its high mechanical and anti-osmosis properties. Contains viracolor.

SUPPORTS

Recommended: Fiberglass polyester and vinylester laminates.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure that the substrate is free of dust, fibers, dirt and surface condensation. Carefully mix the vinylester bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount required depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C. It must be applied manually with a spatula. For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


PLUG
MOULD-LAMINATION
FITTING-OUT

See other Bonding Pastes



GV21

GV21

Vinylester bonding paste with microfibres


Vinylester bonding paste reinforced with microfibers, characterized by remarkable thermal and mechanical properties other than excellent adhesion and flexibility. Specifically formulated to assemble and repair fiberglass laminates, during the lamination phases for filling strips and joints thanks to its excellent adhesion to the substrate and its high mechanical and anti-osmosis properties. Contains viracolor.

SUPPORTS

Recommended: Fiberglass polyester and vinylester laminates.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure that the substrate is free of dust, fibers, dirt and surface condensation. Carefully mix the vinylester bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount required depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C. It must be applied manually with a spatula. For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


LAMINATION-ASSEMBLING
MOULD-LAMINATION
BODY-FINISHING

See other Bonding Pastes



GV20

GV20

Vinylester bonding paste with fibres


Vinylester bonding paste reinforced with glass fibers, characterized by remarkable thermal and mechanical properties other than excellent adhesion and flexibility. Specifically formulated to assemble and repair fiberglass laminates, during the lamination phases for filling strips and joints thanks to its excellent adhesion to the substrate and its high mechanical and anti-osmosis properties. Contains viracolor.

SUPPORTS

Recommended: Fiberglass polyester and vinylester laminates.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure that the substrate is free of dust, fibers, dirt and surface condensation. Carefully mix the vinylester bonding paste with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount required depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C. It must be applied manually with a spatula. For quantities over 5 kg mixing with a stirrer is recommended; for 200 l drums the use of a pressing plate extruder-mixer guarantees the best mixing efficiency.
In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


LAMINATION-ASSEMBLING
FITTING-OUT
BODY-FINISHING

See other Bonding Pastes



G8

G8

Industrial bonding paste with fibres


Multi-purpose bonding paste based on unsaturated polyester resins reinforced with fibres, easily spreadable and with good mechanical properties, adhesion, sandability and flexibility. It is used for filling, assembling and leveling fiberglass products.

SUPPORTS

Recommended: polyester and vinylester fiberglass, wood.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; Make sure the substrate is free of dust, fibres, dirt and surface condensation. Carefully mix the bonding paste with 1,0- 2,0 % of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required. The recommended temperature range is between 12 and 30°C. It must be applied manually with a spatula after careful mixing of the hardener. For quantities over 5 kg, mixing with a stirrer is recommended.
In its original packaging, the product can be used for 12 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


LAMINATION-ASSEMBLING
FITTING-OUT

See other Bonding Pastes



G7

G7

Industrial bonding paste with microfibres


Multi-purpose bonding paste based on unsaturated polyester resins reinforced with microfibres, easily spreadable and with good mechanical properties, adhesion, sandability and flexibility. Is used for filling, assembling and leveling fiberglass products.

SUPPORTS

Recommended: polyester and vinylester fiberglass, wood.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; Make sure the substrate is free of dust, fibres, dirt and surface condensation. Carefully mix the bonding paste with 1,0 – 2,0 % of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required. The recommended temperature range is between 12 and 30°C. It must be applied manually with a spatula after careful mixing of the hardener. For quantities over 5 kg, mixing with a stirrer is recommended.
In its original packaging, the product can be used for 12 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


LAMINATION-ASSEMBLING
FITTING-OUT

See other Bonding Pastes



G6

G6

Bonding paste for assembly


Bonding paste based on unsaturated polyester resins reinforced with special mineral microfibers.
It has good mechanical, thermal and chemical resistance and excellent adhesion to the substrate. In the composite sector, it represents a practical and economical solution for the assembly of the model skeleton, the joining of the side parts, the gluing of the inserts, the fixing of furniture and systems.
It can be used with paste or liquid hardener.

SUPPORTS

Recommended: polyester and vinylester fiberglass, wood.

GENERAL INSTRUCTIONS FOR USE

Make sure the substrate is free of dust, fibres, dirt and surface condensation. Carefully mix the bonding paste with 1,0 – 3,0 % of hardener in paste (benzoyl peroxide) or with 1,0 – 2,0% of liquid hardener (methylethyl ketone peroxide), bearing in mind that the amount of hardener required depends on the temperature of use and the processing times required. The recommended temperature range is between 12 and 30°C. It must be applied manually with a spatula after careful mixing of the hardener. In its original packaging, the product can be used for 12 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.


Packaging

Type of use


MOULD-LAMINATION
LAMINATION-ASSEMBLING
FITTING-OUT

See other Bonding Pastes