Light white putty-gel specifically formulated for fairing the surfaces to the final shape, used for filling and leveling of counterparts and bulkheads, for filling bubbles, defects and bonded joints, smoothing and manual start-up of large surfaces. Particularly suitable for smoothing over 5 mm and for filling where a gel time of more than 25 minutes is required. The excellent leveling and sandability are accompanied by a low shrinkage and an intense white color that facilitates overpainting with gelcoat, significantly increasing the application yield.
To meet the most demanding finishing specifications, it is advisable to add the finishing putty (SG90) to the gelcoat.

SUPPORTS

Recommended: fiberglass laminates, fillers and polyester and vinylester mastics.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure the substrate is free of dust, fibers, dirt and surface condensation. Carefully mix the product with 1,0 – 2,0% of liquid hardener CT21 (methylethyl ketone peroxide), bearing in mind that the quantity of required hardener, depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C. It must be applied manually with a spatula. For further and more specific application details on the putty finishing cycles, refer to “Guidelines for the finishing of the hull”, available at INTEC’s Technical Assistance Center. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.

White gel putty specifically formulated for the composite sector for the finishing and manual leveling of large surfaces.
The excellent workability and sandability are accompanied by a low shrinkage and an intense white color that facilitates overpainting with gelcoat, significantly increasing the application yield. Recommended in a thin layer in bodywork cycles, directly on the support or on top of the filler putty (SG91 filler putty).

SUPPORTS

Recommended: fiberglass laminates, fillers and polyester and vinylester mastics.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure the substrate is free of dust, fibers, dirt and surface condensation. Carefully mix the product with 1,0 – 3,0% of hardener in paste (benzoyl peroxide), bearing in mind that the quantity of required hardener, depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C.
It must be applied manually with a spatula. For further and more specific application details on the putty finishing cycles, refer to “Guidelines for the finishing of the hull”, available at INTEC’s Technical Assistance Center. In its original packaging, the product can be used for 6 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.

Polyester putty for general use characterized by an exceptional spreadability and sandability. Optimal leveling and deaeration for a complete absence of porosity. Used in the composite sector in the finishing of bonded joints, in the repairing of scratches and small cracks, and in the leveling of the surfaces. Its perfect adhesion to any laminate is combined with low shrinkage and excellent sanding properties.

SUPPORTS

Recommended: polyester and vinylester fiberglass laminates; Raw degreased and sanded metal sheet.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure the substrate is free of dust, fibers, dirt and surface condensation. On the sheets, eliminate any residual oxide; degrease with antisilicone thinner. Carefully mix the putty with 1,0 – 3,0% of hardener in paste (benzoyl peroxide), bearing in mind that the quantity of required hardener, depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C.
It must be applied manually with a spatula in one or more layers until the required thickness is reached. Generally recommended dry sanding cycle, grits: P80-P120-P220. In its original packaging, the product can be used for 12 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.

Polyester putty for general use with low specific weight, characterized by an exceptional spreadability and sandability. Optimal leveling and deaeration for a complete absence of porosity. Used in the composite sector in the plug shaping with standard/hand way, in the finishing of bonded joints, in the repairing of scratches and small cracks, and in the leveling of the surfaces. Its perfect adhesion to any laminate is combined with low shrinkage and excellent sanding properties.

SUPPORTS

Recommended: polyester and vinylester fiberglass laminates; Raw degreased and sanded metal sheet.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure the substrate is free of dust, fibers, dirt and surface condensation. On the sheets, eliminate any residual oxide; degrease with antisilicone thinner. Carefully mix the putty with 1,0 – 3,0% of hardener in paste (benzoyl peroxide), bearing in mind that the quantity of required hardener, depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C. It must be applied manually with a spatula in one or more layers until the required thickness is reached. Generally recommended dry sanding cycle, grits: P80-P120-P220. In its original packaging, the product can be used for 12 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.

Lightweight polyester putty applied by spatula.
Used in the composite sector as modeling indicator for the filling of the model and in bodywork for finishing pieces. Being characterized by soft spreadability and excellent sandability without drying out the sandpaper, it is also appreciated for the finishing of bonded joints, the repairing of scratches and small cracks. It has shrinkage, it leaves no surface holes. Its perfect adhesion to any laminate is combined with low shrinkage and excellent sanding properties.

SK21(yellow)
SK21B (white)

SUPPORTS

Recommended: polyester and vinylester fiberglass laminates; Raw degreased and sanded metal sheet.

GENERAL INSTRUCTIONS FOR USE

Apply on well cleaned sanded surfaces; make sure the substrate is free of dust, fibers, dirt and surface condensation. On the sheets, eliminate any residual oxide; degrease with antisilicone thinner. Carefully mix the putty with 1,0 – 3,0% of hardener in paste (benzoyl peroxide), bearing in mind that the quantity of required hardener, depends on the temperature of use and the processing times required. The recommended temperature range of use is between 12 and 30°C.
t must be applied manually with a spatula in one or more layers until the required thickness is reached. Generally recommended dry sanding cycle, grits: P80-P120-P220. In its original packaging, the product can be used for 12 months if stored indoor away from direct sunlight, at temperatures not exceeding 20°C.